Cerințele pentru materiile prime sunt următoarele:
(1) Prăjirea molibdenului necesită S<0.10%, Cu<0.6%, and Pb<0.5%. The actual ingredients are: Mo48.5%~52%, S0.04%~0.07%, P0.01%~0.02%, Cu0.1%~0.5%, Pb0.2%~0.5%, FeO3%~5%, SiO28%~14%, CaO2%~4.5%. 5% to 10% of the total molybdenum is in the form of MoO2, which should be considered when calculating the reaction heat. The particle size is <15mm, of which >10 mm reprezintă mai puțin de 10% și<2mm accounts for about 60%. (2) Ferrosilicon powder contains Si75%~77%; the particle size is <1mm.
Pret pulbere de fero molibden
(3) Aluminum particles contain Al>90% și Cu<0.1%; the particle size is <3mm, and the part <0.5mm shall not exceed 30%.
(4) Iron ore contains Fe>65%, S<0.05%, P<0.05%, C<0.30%; particle size<1mm. Iron oxide scale or iron concentrate can be used instead.
(5) Resturile de oțel sunt resturi de oțel carbon obișnuite, iar lungimea buclei este<50mm.
(6) Fluorite contains CaF2>90%. Dimensiunea particulelor<3mm.
Pret aliaj fero molibden
(7) Saltpeter contains NaNO3>90%. Toate materiile prime trebuie să fie bine uscate și să nu conțină umiditate pentru a evita stropirea și accidentele în timpul procesului de topire. Materiile prime sunt cântărite cu precizie în funcție de proporția calculată, introduse în mixer și amestecate uniform, apoi introduse în cuptorul de topire și topite folosind metoda de aprindere superioară.